    Coercivity and exchange bias in ti-doped maghemite nanoparticles
    (MDPI, 2022) Narayanaswamy, Venkatesha; Al-Omari, Imaddin A.; Kamzin, Aleksandr S.; Khurshid, Hafsa; Khaleel, Abbas; Issa, Bashar; Obaidat, Ihab M.
    Ti-doped maghemite nanoparticles of average crystallite size 12.9 nm were synthesized using the sol-gel method. The XRD profile mainly showed the presence of maghemite phase with very small phases of TiO2 (rutile and anatase). Magnetization hysteresis loops of the nanoparticles were obtained between -4 T to +4 T at temperatures of 2, 10, 30, 50, 70, 100, 150, 200, and 300 K under field cooling (FC) of 1, 2, 3, and 4 T and zero-field cooling conditions (ZFC). The coercivity displayed nonmonotonic field dependence while it decreased sharply with temperature and vanished at 150 K at all fields. Horizontal hysteresis loop shifts were observed in the 2-150 K temperature range in both the ZFC and FC conditions. The exchange bias effect became negligible in both ZFC and FC states above 50 K. Magnetization vs. applied field measurements were conducted in both ZFC and FC cooled conditions at several temperatures in the range of 2-400 K, with spin freezing being observed below 50 K. The exchange bias effect obtained below 50 K is suggested to be attributed to the competing roles of the long-range dipolar and short-range exchange coupled interactions.
  • Küçük Resim Yok
    Öğe
    Evaluation of Antiproliferative Properties of CoMnZn-Fe2O4 Ferrite Nanoparticles in Colorectal Cancer Cells
    (Mdpi, 2024) Narayanaswamy, Venkatesha; Rah, Bilal; Al-Omari, Imaddin A.; Kamzin, Alexander S.; Khurshid, Hafsa; Muhammad, Jibran Sualeh; Obaidat, Ihab M.
    The PEG-coated ferrite nanoparticles Co0.2Mn0.6Zn0.2Fe2O4 (X1), Co0.4Mn0.4Zn0.2Fe2O4 (X2), and Co0.6Mn0.2Zn0.2Fe2O4 (X3) were synthesized by the coprecipitation method. The nanoparticles were characterized by XRD, Raman, VSM, XPS, and TEM. The magnetic hyperthermia efficiency (MH) was determined for PEG-coated nanoparticles using an alternating magnetic field (AMF). X2 nanoparticles displayed the highest saturation magnetization and specific absorption rate (SAR) value of 245.2 W/g for 2 mg/mL in a water medium. Based on these properties, X2 nanoparticles were further evaluated for antiproliferative activity against HCT116 cells at an AMF of 495.25 kHz frequency and 350 G strength, using MTT, colony formation, wound healing assays, and flow cytometry analysis for determining the cell viability, clonogenic property, cell migration ability, and cell death of HCT116 cells upon AMF treatment in HCT116 cells, respectively. We observed a significant inhibition of cell viability (2% for untreated control vs. 50% for AMF), colony-forming ability (530 cells/colony for untreated control vs. 220 cells/colony for AMF), abrogation of cell migration (100% wound closure for untreated control vs. 5% wound closure for AMF), and induction of apoptosis-mediated cell death (7.5% for untreated control vs. 24.7% for AMF) of HCT116 cells with respect to untreated control cells after AMF treatment. Collectively, these results demonstrated that the PEG-coated (CoMnZn-Fe2O4) mixed ferrite nanoparticles upon treatment with AMF induced a significant antiproliferative effect on HCT116 cells compared with the untreated cells, indicating the promising antiproliferative potential of the Co0.4Mn0.4Zn0.2Fe2O4 nanoparticles for targeting colorectal cancer cells. Additionally, these results provide appealing evidence that ferrite-based nanoparticles using MH could act as potential anticancer agents and need further evaluation in preclinical models in future studies against colorectal and other cancers.